Raise3D Industrial PA12 CF Filament - Black - 1.75mm - 1KG

Out of stock
SKU: OC-Rai-7407 Barcode: 6970240723509
Regular price $234.95 CAD
Regular price -8% $254.95 CAD Sale price $234.95 CAD

Do you need help choosing the right material or 3D Printer for your application or require a quote to purchase? Contact Us

3d filament net weight MATERIAL NET WEIGHT: 1KG
Custom sizes may be available, contact us for details.
3d print settings PRINT SETTINGS: SEE BELOW.
Print settings listed in the product description below.
3d data sheet Canada DATA SHEETS & COFC: AVAILABLE UPON REQUEST.
Contact us to inquire about documentation availability.

PA12 CF

A filament for end-use and functional applications

PA12 CF is a Polyamide 12 (PA12,Nylon12)-based 3D printing filament, reinforced with Carbon Fiber. Carbon fiber enhances Nylon’s stiffness, strength, rigidity, shrink ratio, and surface quality, as well as improving chemical and thermal resistance.

  • Outstanding stiffness and strength
  • Excellent heat resistance
  • High hardness
  • Less warp and water uptake

Compatibility: PA12 CF Support, Premium PVA+

Please note, carbon fiber reinforced filament is abrasive and can wear out brass nozzles quickly. It is suggested to print carbon fiber filament with hardened nozzle.

Applications

  • Metal substitute
  • End-use part and tooling
  • Functional parts
  • Manufacture aids
    Raise3D PA12 CF Nylon 3D Printing Filaments Canada


    3d printing temperature guideline Printing
    Temperature:

    Notes:

    280°C - 290°C
    • Nozzle temperature (°C)
      280-290℃
    • Bed temperature (°C)
      60-80℃
    • Layer height (mm)
      0.1-0.25 mm
    • Printing speed (mm/s)
      35-90 mm/s
    • Cooling fan
      ON
    • Drying temperature (°C)
      70°C
    • Printing Notifications:

      • Dry the PA12 CF filament before printing.
      • Use glue stick and turn off cooling fan for improving the first layer adhesion.
      • Set nozzle temperature higher for thin-wall geometry to improve better interlayer bonding and mechanical property.